1. Test Process

Sampling from the defective LSAW steel pipe, and then confirm the location of the defect in the weld seam by manual ultrasonic flaw detector, then processing the weld cross defect section by the method of machining by grinding, polishing, etching after a metallurgical sample. Through the metallurgical test, we can notice the location and quantity of weld slag.

2. Cause Analysis

Theoretically, submerged arc welding seam slag is produced mainly due to the following three points:

A. raw materials inclusions (including base metal, wire, flux)  

B. the multilayer welding interlayer is not clean up  

C. improper selection of welding parameters is not conductive to slag floats.

According LSAW pipe production characteristics can be excluded when the layer of multilayer welding clean up is not clean leaving weld slag produced for this reason.After the raw material for many inclusions leaving produce weld slag, weld inspection before taking the base material, replaced with new wire and flux and other measures, the proportion of weld fusion clamp slag produced only a slight decrease, indicating that the inclusion of raw materials the main reason was not the cause of the slag. Thus, the main reason for the fusion thick wall LSAW pipe clamps slag is produced by improper selection of welding parameters.

Thick wall LSAW pipe welding parameters are: power lines, welding current, welding voltage, welding speed, wire spacing, groove dimensions and so on. Then do in-depth analysis from the welding metallurgy aspects seen: Weld fusion line produced slag is the main reason for the fusion line temperature is too low, the liquid slag late precipitation; and cause fusion line temperature is too low because the peak temperature of the heating or cooling too low too fast.